Microscopic Experimental Investigation on Shear Failure of Solder Joints

A microscopic investigation has been made on the shearing of one leaded and two lead-free solders by using an in situ SEM method. A shear lap joint specimen is designed and fabricated to accommodate a thin layer of solder alloy between copper strips. A non-contact method that measures strains in a very narrow area in the solder was applied. A laser grid was also used on the copper strip for measuring the back-face strain. Simultaneously micrographs at various stages were also taken. Where in situ measurements and micrographs are recorded they can reveal the continual development of damage and fracture mechanisms consistent with observations generated by low-cycle fatigue loading. This means that the shear test can be used as an alternative test to fatigue loading tests. By comparison, two lead-free solder specimens showed much smaller elongation to failure than the leaded solder, although all specimens showed similar sequence of events leading to final failure, including the boundary layer fracture phenomenon. The back-face strain indicator for the formation of a macro crack is due to the shifting of high stress concentration area from the joint-edge region to outside the joint region as revealed by a damage-coupled finite element procedure. The procedure also provides an estimate on the critical back-face strain.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/42763/1/10704_2004_Article_2311.pd

Risk factors for the onset and persistence of neck pain in undergraduate students: 1-year prospective cohort study

<p>Abstract</p> <p>Background</p> <p>Although neck pain is common in young adulthood, studies on predictive factors for its onset and persistence are scarce. It is therefore important to identify possible risk factors among young adults so as to prevent the development of neck pain later in life.</p> <p>Methods</p> <p>A prospective study was carried out in healthy undergraduate students. At baseline, a self-administered questionnaire and standardized physical examination were used to collect data on biopsychosocial factors. At 3, 6, 9, and 12 months thereafter, follow-up data were collected on the incidence of neck pain. Those who reported neck pain on ≥ 2 consecutive follow-ups were categorized as having persistent neck pain. Two regression models were built to analyze risk factors for the onset and persistence of neck pain.</p> <p>Results</p> <p>Among the recruited sample of 684 students, 46% reported the onset of neck pain between baseline and 1-year follow-up, of whom 33% reported persistent neck pain. The onset of neck pain was associated with computer screen position not being level with the eyes and mouse position being self-rated as suitable. Factors that predicted persistence of neck pain were position of the keyboard being too high, use of computer for entertainment < 70% of total computer usage time, and students being in the second year of their studies.</p> <p>Conclusion</p> <p>Neck pain is quite common among undergraduate students. This study found very few proposed risk factors that predicted onset and persistence of neck pain. The future health of undergraduate students deserves consideration. However, there is still much uncertainty about factors leading to neck pain and more research is needed on this topic.</p